moisture-cured

基本解释

A new moisture cure monocomponent polyurethane sealant was prepared by the reaction of hydroxy - termintited polyethers and polyesters with diisocyanate(TDI).
用甲苯二異氰酸酯、聚酯和聚醚通過二步法制備了溼固化單組份聚氨酯密封膠。
The hot-melt moisture cure PU adhesives have been prepared.The effects of the structure of the MDI-polyether prepolymer,tackify resins on peel strength of the adhesives have been studied.
本文制備溼固型MDI-聚醚基聚氨酯熱熔膠,研究了MDI-聚醚預聚物結搆、增粘樹脂等對膠粘劑剝離強度的影響。
Dan Zufen moisture curing, the curing time is not reduced, good flexibility, and strong anti-deformation.
單組份有機矽溼氣固化，固化時不收縮，彈性佳，抗形變能力強。
The moisture curing solventless isocyanate adhesive was prepared form 15% plasiticizer,5% viscosity decrease , molar ratio of PAPI to TDI was 4:1.
最終優化得到的無溶劑型溼固化異氰酸酯膠粘劑的配方組成爲:增塑劑15%25,降粘劑5%25,PAPI與TDI摩爾比爲4:1。
Dan Zufen silicone extrusions moisture curing, the curing time is not reduced, good flexibility, and strong anti-deformation.
單組份有機矽溼氣固化，固化時不收縮，彈性佳，抗形變能力強。